Stainless chromium-titanium steel with ferritic structure X2CrTi12, 1.4512, AISI 409 according to EN 10088-1, EN 10088-2.

 

StandardsSteel Grades
Chemical Composition %
C:Mn:Si:P:S:Cr:Ni:Ti:N:
ENX2CrTi12 - 1.4512 - X 2 CrTi 12
<0.03<1.0<1.0<0.040<0.01510.5 - 12.5-<0.65-
ENX5CrTi12
<0.08<1.0<1.0<0.040<0.03010.5 - 12.5-<1.0 
AFNORZ3CT12 - Z 3 CT 12
<0.03<0.8<0.75<0.040<0.01510.5 - 12.5-<0.6<0.025
SEW 470X7CrTi12 - X 7 CrTi 12 - 1.4720
<0.08<1.0<1.0<0.040<0.03010.5 - 12.5-<1.0-
BS409S19 - 409 S 19
<0.08<1.0<1.0<0.040<0.03010.5 - 12.5<1.0<1.0-
ISOX6CrTi12
<0.08<1.0<1.0<0.040<0.03010.5 - 12.5<0.5<0.65-
UNIX6CrTi12 - X 6 CrTi 12
<0.08<1.0<1.0<0.040<0.03010.5 - 12.5<0.5<0.8-
ASTMAISI 409 - UNS S40900 - TP409
<0.08<1.0<1.0<0.045<0.03010.5 - 11.7<0.5<0.75-

 

X2CrTi12, 1.4512, AISI 409 - specification and application

X2CrTi12 steel is a ferritic grade with an average of 11% chromium and 1% of Titanium in the chemical composition. Produced mostly in the form of sheets, strips and bars, it finds its application mainly in the automotive industry or in the machine industry.

Exhaust systems, small structures, car and other vehicles or machines mufflers are the most common components that are made from the above mentioned grade. None Nickel or its small content in the composition is associated with a ferritic structure, resulting in a relatively higher flue gas resistance.

Materials in the X2CrTi12 grade can work freely for extended periods of time at elevated temperatures of 500 - 600 ℃, which can be classified as heat resistant steel (bypassing standards). Unlike austenitic acid resistant steel, 1.4512 is not resistant to numerous salts, acids or bases.


Mechanical properties of X2CrTi12 / 1.4512 in annealed state:

  • Tensile strength, Rm: 390 - 560 MPa
  • Yield point, Re: > 220 MPa
  • Elongation, A > 20%
  • Modulus of elasticity, E = 220 GPa
  • Heat capacity, cp20℃= 460 J * Kg-1 * K-1
  • Heat conductivity, λ = 25 W * m-1 * K-1
  • Hardness: < 180 HB

Yield point at individual work temperatures

Properties specified in the MPaApproximate properties at temperatures
100℃150℃200℃250℃300℃350℃
Yield pointRe> 200> 195> 185> 180> 180> 160

 


Other properties at elevated temperatures

PropertiesTemperatures
100℃200℃300℃400℃500℃
Modulus of elasticity, E (GPa)215210205195-
Linear Expansion Factor α (10-6 * K-1)10,511,011,512,012,0

 


Heat treatment of X2CrTi12 / 1.4512

  • Annealing at 770 - 830℃ with cooling in water or air
  • Forging and rolling at 1100 - 800℃

 


In the above mentioned grades the company provides:

 


Equivalents and other designations of X2CrTi12:

1.4512, 4512, AISI 409, UNS S40900, UNS S40910, UNS S40920, UNS S40930, SAE 51409, TP409, X2CrTi12, X6CrTi12, X 2 CrTi 12, X 6 CrTi 12, X 6 CrTi 17, X6CrTi12, X6CrTi17, X6CrTi12E, 409S19, 409 S 19, LW12, LW19, X7CrTi12, X 7 CrTi 12, Z3CT12, Z 3 CT 12, F12T, X5CrTi12, X 5 CrTi 12, 00Cr12Ti, 022Cr11Ti, 06Cr11Ti, 0Cr11Ti, F1-25H, F1-45, F1-60, UNS S 40900,


THIS WEBSITE USES COOKIES TO IMPROVE AND FACILITATE YOUR ACCESS TO THE WEBSITE AND TO KEEP STATISTICS. IF YOU CONTINUE TO USE THIS SITE, YOU AGREE THAT THE COOKIES WILL BE STORED ON YOUR DEVICE
PRIVACY POLICY
How do I disable cookies
AGREE