Ferritic stainless steel 0H13, X6Cr13, 1.4000, AISI 410S according to EN 10088-1, PN-71/H-86020.

 

StandardSteel Grade
Chemical Composition %
C:Mn:Si:P:S:Cr:Ni:
ENX6Cr13 - X 6 Cr 13 - 1.4000
<0.08<1.0<1.0<0.040<0.03012.0 - 14.0-
PN0H13
<0.08<0.8<0.8<0.040<0.03012.0 - 14.0<0.6
ASTMUNS S41008 - AISI 410S
<0.08<1.0<1.0<0.040<0.03011.5 - 13.5<0.6
DINX7Cr14 - X 7 Cr 14 - 1.4001
<0.08<1.0<1.0<0.045<0.03013.0 - 15.0-
AFZ8C12 - Z 8 C 12
<0.08<0.75<1.0<0.040<0.01511.5 - 13.0-

 


Stal 0H13, X6Cr13, 1.4000 - specifications and application

X6Cr13 is low-carbon chromium ferritic grade used most often in the oil and coke industries in the form of sheets, rods and strips.

Steel shows resistance to steam, alkaline solutions, acids such as - nitric acid, formic acid, oxalic acid, salts - nitrates, nitrites, carbonates, as well as hot fumes of petroleum, fuels, alcohols, ethers, food products, lubricants, water and oils.

In the case of acids and salts, it should be borne in mind that the X6Cr13 resistance is sufficient at low concentrations of solutions and at low temperatures.

The material is used for the production of rectification columns, cracking pipes, heat exchangers, parts of machinery and equipment in the food industry, and linings of pressure vessels. The steel does not show resistance to intergranular corrosion before and after welding.


Mechanical properties of X6Cr13, 1.4000, 0H13:

  • Tensile strength, Rm: 400 - 630 MPa
  • The yield point, Re: > 230 MPa
  • Elongation, A:> 20%
  • Hardness, HBW: < 200
  • Modulus of elasticity, E = 220 GPa
  • Specific resistance, Ω: 0,6 mkOhm*m
  • Thermal capacity, cp20℃: 460 J * kg-1 * K-1
  • Thermal conductivity, λ: 30 W * m-1 * K-1
  • Linear expansion coefficient, α20℃: 10.5 * 10-6 K-1

 


Mechanical properties at elevated temperatures

PropertiesTemperature (℃)
100200300400500
The yield point, Rp0,2 (MPa)>220>210>200>190-
Linear expansion coefficient, α20℃ (*10-6 K-1)10,511,011,512,012,0
Modulus of elasticity, E (GPa)215210205195-

 


Heat and plastic treatment of X6Cr13, 1.4006, 0H13

 


Other grades designations:

0H13, 1.4000, X6Cr13, AISI 410S, UNS S40300, UNS S41008, AISI 410S, AISI 403, SAE 51403, X 6 Cr 13, SUS410S, F13S, X7Cr14, X 7 Cr 14, Z8C12, Z8C13, Z 8 C 12, Z 8 C13, CSN 17020, 06Cr13, 0Cr13, 08Х13, 08Ch13, 08Kh13