C35E, 1.1181, C35, 1.0501, Ck35 - carbon steel
C35E, 1.1181, C35, 1.0501, Ck35, ct35 - carbon steel in line with EN 10305-1, GOST 1050-13.
| Standard | Grade | ||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Chemical composition % | |||||||||||||||
| C: | Si: | Mn: | P: | S: | Cr: | Mo: | Ni: | ||||||||
| DIN / EN | C35E / Ck35 / 1.1181 | ||||||||||||||
| 0.32-0.39 | <0.4 | 0.5-0.8 | <0.035 | <0.035 | <0.4 | <0.1 | <0.4 | ||||||||
| EN | C35 / 1.0501 | ||||||||||||||
| 0.32-0.39 | <0.4 | 0.5-0.8 | <0.045 | <0.045 | <0.4 | <0.1 | <0.4 | ||||||||
| EN | C35R / 1.1180 | ||||||||||||||
| 0.32-0.39 | <0.4 | 0.5-0.8 | <0.03 | 0.02-0.04 | <0.4 | <0.1 | <0.4 | ||||||||
| PN | 35 | ||||||||||||||
| 0.32-0.39 | 0.1-0.4 | 0.5-0.8 | <0.04 | <0.04 | <0.3 | <0.1 | <0.3 | ||||||||
| GOST | ct35 | ||||||||||||||
| 0.32-0.40 | 0.17-0.37 | 0.5-0.8 | <0.035 | <0.04 | <0.4 | - | <0.4 | ||||||||
| NF | XC38 | ||||||||||||||
| 0.32-0.39 | <0.4 | 0.5-0.8 | <0.03 | <0.035 | <0.4 | <0.1 | <0.4 | ||||||||
| BS | 080M36 | ||||||||||||||
| 0.32-0.40 | 0.1-0.4 | 0.6-1.0 | <0.05 | 0.015-0.050 | - | - | - | ||||||||
| STAS | OLC35X | ||||||||||||||
| 0.32-0.39 | 0.17-0.37 | 0.5-0.8 | <0.035 | <0.035 | <0.3 | - | <0.3 | ||||||||
| ASTM | AISI 1035 - UNS G10350 | ||||||||||||||
| 0.32-0.38 | - | 0.6-0.9 | <0.04 | <0.05 | - | - | - | ||||||||
C35E, 1.1181, C35, 1.0501, Ck35 - description
Unalloyed quality steel used in normalized, toughened and case-hardened condition. It is used to produce light-loaded machine parts, axles, shafts, crankshafts, levers, cylinders, piston rods, gears, wedges and fasteners.
The alloy has medium strength, high ductility and limited weldability.
Physical and mechanical properties
- Forgings general properties according to EN 10250-2
- in normalized condition (+N) and normalized / tempered (+NT):
- Rm: > 500 MPa
- Re: > 245 MPa
- A: > 19 %
- KV, 20°С: > 19 J
- in toughened condition (+QT):
- Rm: > 470 MPa
- Re: > 270 MPa
- A: > 21 %
- KV, 20°C: > 25 J
- in normalized condition (+N) and normalized / tempered (+NT):
- Bars and flat products general properties according to EN 10083-2:
- in normalized condition (+N):
- Rm: > 520 MPa
- Re: > 270 MPa
- A: > 19 %
- in toughened condition (+QT):
- Rm: 550-780 MPa
- Re: > 320 MPa
- A: >19 %
- Z: > 45 %
- KV, 20°C: > 35 J
- in normalized condition (+N):
- Tubes general properties according to EN 10297-1 and EN 10305-1
- hot-rolled, normalized (+N), according to EN 10297-1:
- Rm: > 520 MPa
- Re: > 270 MPa
- A: > 17 %
- hot-rolled, toughened (+QT) according to EN 10297-1:
- Rm: > 500 MPa
- Re: >290 MPa
- A: > 20 %
- cold-drawn, according to EN 10305-1:2010:
- Tubes +C - Rm: >590 MPa
- Tubes +LC - Rm: >540 MPa
- Tubes +A - Rm: >440 MPa
- Tubes +N - Rm: >460 MPa
- hot-rolled, normalized (+N), according to EN 10297-1:
- Cold-drawn strips according to EN 10132-3:
- In annealed condition (+A+LC)
- Rm: > 500 MPa
- Re: > 290 MPa
- A: > 18 %
- Hardness: < 170 HV
- Hardness: < 86 HRB
- In hardened condition (+CR)
- Rm: < 930 MPa
- Hardness: < 275 HV
- In annealed condition (+A+LC)
Heat treatment and working
Recommended working and heat treatment parameters for C35E alloy:
- Soft annealing: 650-700 °C
- Quenching: 840-880 °C
- Stress relieving: 550-680 °C
- Normalizing: 860-900 °C
We deliver this steel alloy as:
- Bars
- Forgings
- Tubes and pipes
- coldrolled strips
Substitutes, equivalents and other species designations
C35E
35
C35R
XC38
Cf35
Ck35
080M36
MC
OLC35X
G10350
C1431
1.1181
1572
Dauphin CV4
Talabot XC35H1
N4
XC38H1
2C35
A-1130
F1120
Almenit 1181
Bohler V935
DIRO-C 35E
EW Ck35
Guete Ck35
Klockner C35E
Thyrofort C35E
UHB C35E
BGH 1181
Buderus C35E
EW 1181
Eschmann Ck35
IS 1181
OVAKO 037A
TS Ck35
Need help? Contact us!
Call or send a message, and our representative
will contact you within 24 hours!
Write
Call